HDPE Geomembrane

Trademark: CHANGYI
Origin: China
Customization:

Contact Supplier

Gold Member Since 2011

Suppliers with verified business licenses

Product Description

GM SH series of geomembrane is made by high density polyethylene resins. The surface of both sides are smooth. The product is manufactured by the technology of coextrusion-brown triple layer. It provides geomembranes with specific proporties on each layer, e. G. Bioclolor or textured designs.

Performance:
Excellent physical and merchanic performance. High tearing resistance. Good deformation adaptability. High puncture resistance. High aging resistance. High UV rsistance. Anti-acid&alkali. Excellent low&high temperature resistance. Innocuous, long life span. Perfect water proof performance. Seepage and humidity resistance.

Voluntary standards:
GRI-GM13

Application:
The project of landfill site, bank, dam, storage reservoir, channel, irrigation, highway, railway, tunnel, drinking tank, salt field bittern pan, chemical liquid storage, treatment tank, artificial lake and riverway, etc.
Properties Test Method GM SH075 GM SH100 GM SH125 GM SH150 GM SH200 GM SH250
Thickness D5199 0.75mm 1.00mm 1.25mm 1.50mm 2.00mm 2.50mm
Density D1505 0.940g/cc 0.940g/cc 0.940g/cc 0.940g/cc 0.940g/cc 0.940g/cc
Tensile Properties                                                1. Yeild strength                                                    2. Break strength                                                    3. Yeild elongation                                                4. Break elongation D6693    Type IV 11KN/m 20KN/m 12%      700% 15KN/m 27KN/m 12%      700% 18KN/m 33KN/m 12%      700% 22KN/m 40KN/m 12%      700% 29KN/m 53KN/m 12%      700% 37KN/m 67KN/m 12%      700%
Tear Resistance D1004 93N 125N 156N 187N 249N 311N
Puncture Resistance D4833 240N 320N 400N 480N 640N 800N
Stress Crack Resistance D5397(App. ) 300 hr. 300 hr. 300 hr. 300 hr. 300 hr. 300 hr.
Carbon Black Content D1603 2.0% 2.0% 2.0% 2.0% 2.0% 2.0%
Carbon Black Dispersion D5596 Note (1) Note (1) Note (1) Note (1) Note (1) Note (1)
Oxidative Induction Time (OIT) D3895 100min. 100min. 100min. 100min. 100min. 100min.
Width  2 ~ 7m
Note (1): Carbon black dispersion (only near spherical agglomerates) for 10 different views: 9 in catalogue 1 or 2, and 1 in catalogue 3.
 